High density tungsten alloy balls for counterweight
Tungsten nickel iron/copper(WNiFe&WNiCu) alloy balls/shots
Material: W90NiCu, W90Ni7Fe3, W92NiCu, W92.5NiFe, W95NiFe, W97Ni2Fe1
1) Density of tungsten shot: 17g-18.5g/cm3
2) Available size: Dia: 2.0mm,dia2.25mm,dia2.5mm,dia3.0mm,dia3.5mm,dia4.0mm,dia4.5mm,
dia5.0mm,dia5.5mm,dia6.0mm,dia6.5mm and so on,the biggest size is dia15mm
High density Tungsten based alloy
Tungsten Alloy Density: (17~18.5)
Tungsten Alloy component: W(88-98)% with the addition of nickel and copper or nickel and iron, etc
Tungsten Alloy applications: For making rotors of aircraft wings, shileding materias for radioactive isotope (Cobalt 60), and formaterials of armor piercing bullets and mould, etc.
| Class |
Nominal tungsten (weight percent) |
Density (g/cc) |
Hardness ( HRC )(maximum) |
| 1 |
90 |
16.85 - 17.25 |
32 |
| 2 |
92.5 |
17.15- 17.85 |
33 |
| 3 |
95 |
17.75- 18.35 |
34 |
| 4 |
97 |
18.25- 18.85 |
35 |
We also have other tungsten carbide products:
Tungsten Carbide ball/tungsten caride shot
The tungsten carbide alloy ball/shot:
1. Tungsten nickel iron/copper(WNiFe&WNiCu) alloy balls/shots
Material: W95NiCu, W95NiFe, W90Ni7Fe3, W92Ni5Cu3, W92.5NiFe, W97Ni2Fe1, etc.
2. Tungsten carbide alloy balls/shots
Grade: YG6 YG6X YG8 YG10 or as customers' requirements
Material: WC94% Co6%, WC92% Co8, etc
Property: Good Wear Resistance,High Hardness
3. Tungsten shots/balls specification:
1) Density of tungsten shot: 17g-18.5g/cm3
2) Available size:
Dia2.0mm, dia2.25mm, dia2.5mm, dia3.0mm, dia3.5mm, dia4.0mm, dia4.5mm, dia5.0mm, dia5.5mm, dia6.0mm, dia6.5mm and dia10mm, etc., and the biggest size is dia15mm.
Tungsten carbide alloy grade:
| Grade |
Binder (Wt %) |
Density (g/cm3) |
Hardness (HRA) |
TRS (≥N/mm²) |
| YG6 |
6 |
14.8 |
90.0 |
1520 |
| YG6X |
6 |
14.9 |
91.0 |
1450 |
| YG6A |
6 |
14.9 |
92.0 |
1540 |
| YG8 |
8 |
14.7 |
89.5 |
1750 |
| YG12 |
12 |
14.2 |
88.0 |
1810 |
| YG15 |
15 |
14.0 |
87.0 |
2050 |
| YG20 |
20 |
13.5 |
85.5 |
2450 |
| YG25 |
25 |
12.1 |
84.0 |
2550 |