90%Wnife, 90%Wnicu Tungsten Copper Alloy Tungsten High Heavy Alloy

• Product Type: Rod
• Material: Tungsten Alloy
• Carbon Content: Low Carbon
• Model NO.: alloy rods
• PCD: 100mm
• ET: No
• Hole: No
• Density: >17.2g/cm3
• Grade: W90nife W92nife W95nife W97nife
• Transport Package: Wooden Box
• Specification: Dia(1-10mm)*L (150, 175, 200, 800-1000)
• Trademark: Jiangchi
• Origin: China
• HS Code: 8101990000
• Production Capacity: 100t/Year
• Package Size: 52.00cm * 18.00cm * 15.00cm
• Package Gross Weight: 5.000kg

Product Description

High Quality Tungsten High Heavy Alloy ASTM B777-07 rods/sheet/tubes
High Quality Tungsten High Heavy Alloy
ASTM B777-07  rods/sheet/tubes/rings/discs/wafer/special drawing, etc.
Material:
W90-97NiFe(Magnetic) & W90-97NiCu(Nonmagnetic)
Density:16.8-18.8g/cm3
High density Tungsten based alloy
-Tungsten Nickel Iron Alloy
-Tungsten Nickel Copper Alloy
Tungsten Alloy Density: (17~18.5)g/cm3
Tungsten Alloy component: W(88-98)% with the addition of nickel and copper or nickel and iron, etc
Tungsten Alloy applications: For making rotors of aircraft wings, shileding materias for radioactive isotope (Cobalt 60), and formaterials of armor piercing bullets and mould, etc.
Production Method 
1), Blending of tungsten powder with other metal powders and a bonding agent, cooling and sieving. 
2), Pressing the blended powder to the required shape (allowing for shrinkage during the final processing), and shaping the green part component. 
3). Pre-sintering the pressed components to remove the bonding agent. 
Final sintering in the hydrogen fed furnace to fuse the powder particles together. 
4). Supplied in bar, square, round and rectangle sizes are available in rough oversize, or turned or ground to exact requirements. Components can also be produced to customer drawings. 
High Heavy Tungsten nickel iron/ tungsten nickel copper(WNiFe&WNiCu) alloy 
Material: W90NiCu, W90Ni7Fe3, W92NiCu, W92.5NiFe, W95NiFe, W97Ni2Fe1, etc.

Class	Nominal tungsten (weight percent)	Density    (g/cc)	Hardness ( HRC )(maximum)
1	90	16.85 - 17.25	32
2	92.5	17.15- 17.85	33
3	95	17.75- 18.35	34
4	97	18.25- 18.85	35

Material:W90-97NiFe(Magnetic)&W90-97NiCu(Nonmagnetic)
Density:16.8-18.8g/cm3
Property of tungsten alloy
AMST 21014 class 1
90%WNiFe, 90%WNiCu
Density : 17.0
Hardness: 32HRC max
Elongation: 5-20%

AMST 21014 class 2
92.5%WNiFe, 92.5%WNiCu
Density : 17.2
Hardness: 33HRC max
Elongation: 5-15%

AMST 21014 class 3
95%WNiFe, W95NiCu
Density : 18.0
Hardness: 34HRC max
Elongation: 3-10%

AMST 21014 class 4
97.5%WNiFe, W97.5NiCu
Density : 18.85
Hardness: 35HRC max
Elongation: 1-8%
Tungsten high heavy alloy
- Material: W90-97NiFe(Magnetic) & W90-97NiCu(Nonmagnetic)
        - Density:16.8-18.8g/cm3
        - Rods Size:dia(1.5 -200) x Length<500mm  
         Plate size: 0.1min Thickness*W*L

1. Tungsten copper alloy rod Specification:
Material: W50-90Cu10-50
Density: 11.85g/cm3-16.75g/cm3
Product standard: GB8320-87
WCu alloy foil size: Thickness(0.08-0.7mm)*Width<120mm*Length<300mm
WCu alloy sheet size: diameter(3-100mm)*L<500mm

2. Pure tungsten/molybdenum rod surface finish:
Black: surface is as swaged or as drawn, retaining a ciating of processing lubricants and oxides.
Cleaned: Surface is chemically cleaned to removed all lubricants and oxides.
Ground: Surface is centerless to ground to remove all coating and to achieve precise diameter control.

3. Pure tungsten rod dimension:

Tungsten Content	Type	Diameter (mm)	Dia.Tolerance (mm)	Length (mm)	L tolerance (mm)
99.95%	Sintering rod	40-100	±3	500max	±5
99.95%	Froged rod	20-80	±2	800max	±5
99.95%	Ground rod	2-60	±0.1	600max	±1

Tungsten rods available size:
Forged rods size: Diameter(2-100mm)*Length<2500mm
Strainghtened rods after drawn  diameter 0.8-3.2mm

4. Chemical composition

Content of Tungsten	Content of all other elements	Content of each element
≥99.95%	≤0.05%	≤0.01%

5. Application & Features
  Used as electrodes in the field of rare earth metal industry;
  For producing electric light source parts and electric vacuum components;
  Used in electric boosting glass kiln electrode;
  Suitable for producing ion implantation parts;
  For producing heating elements and refractory parts in high teperature furnaces;
  Very good interlaminar strength at strong thermal and mechanical loadings
6. More information about us:
We promise you -- The advantage of us:
 1) products quality, with many years of producing experience
 2) low price in the market, and factory direct sales.
 3) the whole production line from powder to finished products, top and steady quality assured
 4) good packing for safe exprot delivery, and fast manufacturing time
 5) fast delivery and best after-sale service.