W (88-98) % with The Addition of Nickel and Copper/Iron Wnicu Wnife High Density Heavy Tungsten High Alloy Rod

• Customization: Available
• Density: >12.2g/cm3
• Grade: W90nife W92nife W95nife W97nife
• Model NO.: w alloy
• Product Type: Rod
• Carbon Content: Low Carbon
• PCD: 100mm
• Material: Tungsten Alloy
• ET: No
• Hole: No
• Transport Package: Wooden Box
• Specification: Dia(1-10mm)*L (150, 175, 200, 800-1000)
• Trademark: Jiangchi
• Origin: China
• HS Code: 8101990000
• Production Capacity: 100t/Year
• Package Size: 22.00cm * 22.00cm * 12.00cm
• Package Gross Weight: 3.000kg

Product Description

Tungsten alloy products: rod/plate/sheet/bar/tube/ring/special shape products
High Quality Tungsten High Heavy Alloy ASTM B777-07  rods/sheet/tubes/rings/discs/wafer/special drawing, etc.
Material:
W90-97NiFe(Magnetic) & W90-97NiCu(Nonmagnetic)
Density:16.8-18.8g/cm3
High density Tungsten based alloy
-Tungsten Nickel Iron Alloy
-Tungsten Nickel Copper Alloy
Tungsten Alloy Density: (17~18.5)g/cm3
Tungsten Alloy component: W(88-98)% with the addition of nickel and copper or nickel and iron, etc
Tungsten Alloy applications: For making rotors of aircraft wings, shileding materias for radioactive isotope (Cobalt 60), and formaterials of armor piercing bullets and mould, etc.
Production Method 
1), Blending of tungsten powder with other metal powders and a bonding agent, cooling and sieving. 
2), Pressing the blended powder to the required shape (allowing for shrinkage during the final processing), and shaping the green part component. 
3). Pre-sintering the pressed components to remove the bonding agent. 
Final sintering in the hydrogen fed furnace to fuse the powder particles together. 
4). Supplied in bar, square, round and rectangle sizes are available in rough oversize, or turned or ground to exact requirements. Components can also be produced to customer drawings. 
High Heavy Tungsten nickel iron/ tungsten nickel copper(WNiFe&WNiCu) alloy 
Material: W90NiCu, W90Ni7Fe3, W92NiCu, W92.5NiFe, W95NiFe, W97Ni2Fe1, etc.

Class	Nominal tungsten (weight percent)	Density    (g/cc)	Hardness ( HRC )(maximum)
1	90	16.85 - 17.25	32
2	92.5	17.15- 17.85	33
3	95	17.75- 18.35	34
4	97	18.25- 18.85	35

Tungsten Copper Tungsten alloy WCu plate/sheet/bar
1. WCu tungsten alloy specification:
  1) WCu (W70Cu, W75Cu, W80Cu, W85Cu, W90Cu, etc)
  2) Density:16-18.8g/cm3
  3) Size:As your need
    Plate: (0.04-50)* W X L
    rod-Dia.1.5 - 200 X 300mm Long
  4) Flatness tolerance:<4um
  5) Roughness:Ra1.6-Ra0.8
  6) Surface: polished, ground.
2. Property Brief Introduction
W-Cu heat sink material is a composite of tungsten and copper, with both tungsten low expansion characteristics, but also has copper of high thermal conductivity properties, and the tungsten and copper in the thermal expansion coefficient and thermal conductivity can be adjusted with the W-Cu composition, also the composite can be machined to various shape, these features make the application of this composite with great convenience.
 1) high melting point, high strength,
 2) smooth and clean surface,
 3) good conductions, small linear expansion coefficient and good heat-resistance

3. Chemical composition

Material	WCu% Tungsten Content	Hardness HB	g/ Density at 20ºC	W/M.K Thermal conductivity at 25ºC	(10-6/k) Coefficient of thermal expansion at 20ºC
W90Cu10	90	260	17.0	180-190	6.5
W85Cu15	85	240	16.4	190-200	7.0
W80Cu20	80	220	15.6	200-210	8.3
W75Cu25	75	195	14.9	220-230	9.0
W50Cu50	50	125	12.2	310-340	12.5

W50-W90% wolfram tungsten copper alloy plate supplier 
Material: W50-90Cu10-50
Density: 11.85g/cm3-16.75g/cm3
Product standard: GB8320-87
WCu alloy foil size: Thickness(0.08-0.7mm)*Width<120mm*Length<300mm
WCu alloy sheet size: the main sizes see attachment
WCu alloy rods size: diameter(3-100mm)*L<500mm

4. WCu alloy Tungsten Copper alloy--Tungsten Copper Composite Features:
No Fe, Co, Ni, Mn and other elements added as the sintering activator, to maintain a high thermal conductivity
Excellent hermeticity
Can provide semi-finished or finished (Ni/Au plated) products
Precision machining and excellent dimensional control, surface finish and flatness
With close technical support including product design, custom manufacturing, testing and post sale supports.
High Quality Tungsten High Heavy Alloy ASTM B777-07 rods/sheet/tubes
Material:W90-97NiFe(Magnetic)&W90-97NiCu(Nonmagnetic)
Density:16.8-18.8g/cm3
Property of tungsten alloy
AMST 21014 class 1
90%WNiFe, 90%WNiCu
Density : 17.0
Hardness: 32HRC max
Elongation: 5-20%

AMST 21014 class 2
92.5%WNiFe, 92.5%WNiCu
Density : 17.2
Hardness: 33HRC max
Elongation: 5-15%

AMST 21014 class 3
95%WNiFe, W95NiCu
Density : 18.0
Hardness: 34HRC max
Elongation: 3-10%

AMST 21014 class 4
97.5%WNiFe, W97.5NiCu
Density : 18.85
Hardness: 35HRC max
Elongation: 1-8%
Tungsten high heavy alloy
- Material: W90-97NiFe(Magnetic) & W90-97NiCu(Nonmagnetic)
        - Density:16.8-18.8g/cm3
        - Rods Size:dia(1.5 -200) x Length<500mm  
         Plate size: 0.1min Thickness*W*L

1. Tungsten copper alloy rod Specification:
Material: W50-90Cu10-50
Density: 11.85g/cm3-16.75g/cm3
Product standard: GB8320-87
WCu alloy foil size: Thickness(0.08-0.7mm)*Width<120mm*Length<300mm
WCu alloy sheet size: diameter(3-100mm)*L<500mm

2. Pure tungsten/molybdenum rod surface finish:
Black: surface is as swaged or as drawn, retaining a ciating of processing lubricants and oxides.
Cleaned: Surface is chemically cleaned to removed all lubricants and oxides.
Ground: Surface is centerless to ground to remove all coating and to achieve precise diameter control.

3. Pure tungsten rod dimension:

Tungsten Content	Type	Diameter (mm)	Dia.Tolerance (mm)	Length (mm)	L tolerance (mm)
99.95%	Sintering rod	40-100	±3	500max	±5
99.95%	Froged rod	20-80	±2	800max	±5
99.95%	Ground rod	2-60	±0.1	600max	±1

Tungsten rods available size:
Forged rods size: Diameter(2-100mm)*Length<2500mm
Strainghtened rods after drawn  diameter 0.8-3.2mm

4. Chemical composition

Content of Tungsten	Content of all other elements	Content of each element
≥99.95%	≤0.05%	≤0.01%

5. Application & Features
  Used as electrodes in the field of rare earth metal industry;
  For producing electric light source parts and electric vacuum components;
  Used in electric boosting glass kiln electrode;
  Suitable for producing ion implantation parts;
  For producing heating elements and refractory parts in high teperature furnaces;
  Very good interlaminar strength at strong thermal and mechanical loadings
6. More information about us:
We promise you -- The advantage of us:
 1) products quality, with many years of producing experience
 2) low price in the market, and factory direct sales.
 3) the whole production line from powder to finished products, top and steady quality assured
 4) good packing for safe exprot delivery, and fast manufacturing time
 5) fast delivery and best after-sale service